Clay Analysis

ANALYSIS RESULTS KA-502 (102)

 

Item

Unit

Result

Method Used / Relevant Standards

Chemical Properties

K.K.

%

8.15

FOR IGNITION LOSS: TM.LT.02 (internal method based on TS.2980 and TS.3245) - (Based on TS 2980:1978 and TS 3245:1978). FOR ANALYSIS WITH XRF: TM.LT.04 (Internal method based on EN 15039)

SiO2

%

56.85

Al2O3

%

26.34

Fe2O3

%

3.18

TiO2

%

1.1

CaO

%

0.21

MgO

%

0.97

Na2O

%

0.2

K2O

%

2.95

 

ANALYSIS RESULTS KA-502 (102)

 

Item

Unit

Result

Method Used / Relevant Standards

Tile Properties

BAKING TEMPERATURE

oC

1180

 

DRY TILE RESISTANCE

kgf/cm2

29.693

 

KILN TYPE

 

EKS

PRESSURE

Bar

320

BAKING PERIOD

Min.  

27

TOTAL SHRINKING

%

10.951

WATER ABSORPTION

%

0.778

BAKING RESISTANCE

kgf/cm2

589.43

BLACK CORE

 

Baked Color

L

Lightness-Darkness

63.78

 

a

+Red,-Green

4.57

 

b

+Yellow,-Blue

17.38

 

Y

Yellow

33.84

 

 

ANALYSIS RESULTS KA-103

 

Item

Unit

Result

Method Used / Relevant Standards

Chemical Properties

K.K.

%

7.45

FOR IGNITION LOSS: TM.LT.02 (internal method based on TS.2980 and TS.3245 ) - (Based on TS 2980:1978 and TS 3245:1978). FOR ANALYSIS WITH XRF: TM.LT.04 (Internal method based on EN 15039)

SiO2

%

59.8

Al2O3

%

24.4

Fe2O3

%

2.77

TiO2

%

1.13

CaO

%

0.23

MgO

%

0.88

Na2O

%

0.35

K2O

%

2.98

 

 

ANALYSIS RESULTS KA-103

 

Item

Unit

Result

Method Used / Relevant Standards

Tile Properties

BAKING TEMPERATURE

oC

1180

 

DRY TILE RESISTANCE

kgf/cm2

35.52

 

KILN TYPE

 

EKS

PRESSURE

Bar

320

BAKING PERIOD

Min.

27

TOTAL SHRINKING

%

9.073

WATER ABSORPTION

%

1.439

BAKING RESISTANCE

kgf/cm2

531.56

BLACK CORE

 

Baked Color

L

Lightness-Darkness

66.64

 

a

+Red,-Green

4.97

 

b

+Yellow,-Blue

17.45

 

Y

Yellow

32.94

 

 

 

ANALYSIS RESULTS KA-107

 

Item

Unit

Result

Method Used / Relevant Standards

Chemical Properties

K.K.

%

7.1

FOR IGNITION LOSS: TM.LT.02 (internal method based on TS.2980 and TS.3245 ) - (Based on TS 2980:1978 and TS 3245:1978). FOR ANALYSIS WITH XRF: TM.LT.04 (Internal method based on EN 15039)

SiO2

%

60.68

Al2O3

%

22.325

Fe2O3

%

3.76

TiO2

%

1.27

CaO

%

0.195

MgO

%

0.965

Na2O

%

0.435

K2O

%

3.22

 

ANALYSIS RESULTS KA-107

 

Item

Unit

Result

Method Used / Relevant Standards

Baked Color

L

Lightness-Darkness

58.11

 

a

+Red,-Green

3.84

 

b

+Yellow,-Blue

17.18

 

Y

Yellow

36.08

 

Casting Properties

Casting Concentration

%

66.66

 

ELECTROLYTE 5 Poise

ml/100gr

0.6

 

THIXOTROPY

 

2.25

 

LITER WEIGHT

gr/lt

1741

 

DRY BINDING RESISTANCE

kg/cm2

57.5

 

DRY SHRINKING

%

4.38

 

Baking Properties

TOTAL SHRINKING

%

12.25

 

WATER ABSORPTION

%

0

 

 

ANALYSIS RESULTS KA-107

 

Item

Unit

Result

Method Used / Relevant Standards

Tile Properties

BAKING TEMPERATURE

oC

1210

 

DRY TILE RESISTANCE

kgf/cm2

27.348

 

KILN TYPE

 

EKS

PRESSURE

Bar

350

BAKING PERIOD

Min.

56

TOTAL SHRINKING

%

8.39

WATER ABSORPTION

%

2.71

BAKING RESISTANCE

kgf/cm2

458. 6

BLACK CORE

 

Baked Color

L

Lightness-Darkness

57.54

 

a

+Red,-Green

8.55

 

b

+Yellow,-Blue

17.88

 

Y

Yellow

37.5

 

 

ANALYSIS RESULTS KA-112

 

Item

Unit

Result

Method Used / Relevant Standards

Tile Properties

BAKING TEMPERATURE

oC

1220

 

DRY TILE RESISTANCE

kgf/cm2

47.72

 

BAKING PERIOD

Min.

70

TOTAL SHRINKING

%

10.04

WATER ABSORPTION

%

0.017

BAKING RESISTANCE

kgf/cm2

158

BLACK CORE

 

Baked Color

BAKING TEMPERATURE

oC

1220

 

L

Lightness-Darkness

65.96

 

a

+Red,-Green

1.8

 

b

+Yellow,-Blue

15.79

 

Y

Yellow

30.2

 

 

 

ANALYSIS RESULTS KA-112

 

Item

Unit

Result

Method Used / Relevant Standards

Chemical Properties

K.K.

%

7.68

FOR IGNITION LOSS: TM.LT.02 (internal method based on TS.2980 and TS.3245 ) - (Based on TS 2980:1978 and TS 3245:1978). FOR ANALYSIS WITH XRF: TM.LT.04 (Internal method based on EN 15039)

SiO2

%

60.41

Al2O3

%

25

Fe2O3

%

1.845

TiO2

%

1.055

CaO

%

0.2

MgO

%

0.83

Na2O

%

0.06

K2O

%

2.89